鋁板廠家如何區(qū)別拉絲鋁板和氧化鋁板？對(duì)于初次接觸鋁板的朋友來(lái)說(shuō)，如何區(qū)分鋁板的類(lèi)別是一個(gè)不小的挑戰(zhàn)，作為鋁板生產(chǎn)廠家為您排憂解難是我們義不容辭的責(zé)任，就較常見(jiàn)的拉絲鋁板和氧化鋁版給您詳細(xì)介紹下。
　　How does aluminium plate manufacturer distinguish wire drawing aluminium plate from alumina plate? For the first time contact with aluminium plate friends, how to distinguish the type of aluminium plate is a big challenge. As an aluminium plate manufacturer, it is our duty to help you solve the problems. The most common drawing aluminium plate and alumina plate are introduced in detail.
　　拉絲鋁板：反復(fù)用砂紙將鋁板刮出線條的制造過(guò)程，其工藝主要流程分為脫酯、沙磨機(jī)、水洗3個(gè)部分。在鋁板拉絲制程中，陽(yáng)出彩處理之后的特殊的皮膜技術(shù)，可以使鋁板表面生成一種含有該金屬成分的皮膜層，清晰顯現(xiàn)每一根細(xì)微絲痕，從而使金屬啞光中泛出細(xì)密的發(fā)絲光澤。
　　Wire drawing aluminium sheet: The manufacturing process of scraping aluminium sheet out of line repeatedly with sandpaper. Its main process is divided into three parts: deesterification, sand mill and water washing. In the process of drawing aluminium sheet, the special skin film technology after anodic treatment can make the surface of aluminium sheet produce a kind of skin film containing this metal component, which can clearly show each fine filament mark, and thus make the metal glossy and lustrous.
　　拉絲鋁板的系列很多，不同系列的具有自己獨(dú)特的鋁板屬性，具體表現(xiàn)在他的拉絲效果、抗腐蝕性、抗污性，那么這些性能的具備當(dāng)然需要有時(shí)候在拉絲的過(guò)程中加入部分氧化性，但是這不等同于拉絲鋁板就是氧化鋁板，這樣是不科學(xué)的。
　　There are many series of wire drawing aluminium sheets. Different series have their own unique properties of aluminium sheets, which are embodied in their drawing effect, corrosion resistance and contamination resistance. It is of course necessary to add some oxidation in the process of wire drawing, but this is not the same as that of aluminium sheet, which is not scientific.
　　氧化鋁板：將鋁板置于相應(yīng)電解液(如硫酸、鉻酸、草酸等)中作為陽(yáng)出彩，在特定條件和外加電流作用下，進(jìn)行電解而形成的鋁板。陽(yáng)出彩的鋁板氧化，表面上形成氧化鋁薄層，其厚度為5～20微米，硬質(zhì)陽(yáng)出彩氧化膜可達(dá)60～200微米。

                                
　　Alumina plate: Aluminum plate is formed by electrolysis of aluminum plate in corresponding electrolyte (such as sulphuric acid, chromic acid, oxalic acid, etc.) as an anode under specific conditions and applied current. A thin layer of alumina is formed on the surface of the anode when the aluminium plate is oxidized. Its thickness is 5-20 microns, and the hard anodic oxide film can reach 60-200 microns.
　　氧化鋁板也同樣有很多系列，但是他們都有一個(gè)共同特點(diǎn)就是表面都是具有氧化膜的鋁板，他的表面跟具有拉絲紋理的拉絲鋁板有截然不同。
　　There are also many series of alumina sheets, but they all have a common feature that the surface is aluminium sheets with oxide film, and its surface is quite different from that of aluminium sheets with drawing texture.